Sample preparation for plastic sector depends on the material properties and shape of material is going to be tested. First question is that what do you want to test? if it is a raw material or it is finished product? If you want to test raw material, be sure that you will be testing the…
38. Stiffness of Fabric 38.4 Apparatus:38.4.1 CRE-Type Tensile Testing Machine.38.4.2 Loading Cell, 20 N (2000 gf).38.4.3 Specimen Holder—An 85-mm (33⁄8-in.) square frame made of 5-mm (1⁄4-in.) diameter steel rod. In the middle of one side is a hook made of 3-mm (1⁄8-in.) rod diameter for connecting the holder to the loading cell. In the middle…
4 Apparatus 4.1 The apparatus used for the test should be designed to comply with the following conditions. 4.1.1 It should be possible to clamp the specimen of fabric in such a way that a) it is horizontal and is not bulging; b) an area of the fabric of 100 cm2 * is subjected to…
12.12 Resistance to Impact of the Coating 12.12.1 EquipmentThe equipment shall consist of the following:(a) an impact tester having the following features:(i) 1 kg falling mass;(ii) 15.8 mm diameter ball-bearing tup;(iii) 1 m long graduated slotted tube;(iv) for laboratory-coated specimen testing, flat anvils hardened to 55 ± 5 HRC;(v) for testing specimens from test rings,…
8. Requirements 8.1 Longitudinal Reversion—When tested in accordance with ISO 15874-2, at the conditions given in Table 8, the mean relative change in pipe length shall not exceed 2 %. 8.2 Melt Flow Rate (MFR) of Pipe and Fittings—When tested in accordance with D 1238, the MFR of specimens taken from the finished pipe or…
C.1 GeneralThe test shall consist of measuring the force required for peeling the coating from the metal substrate of the pipe at a constant rate of pull.C.2 EquipmentC.2.1 Tensile testing machine, capable of recording the peel force with a 5 % reading accuracy, thatoperates at a rate of pull of 10 mm/min, as shown in…
6.4 Pipe Stiffness and Flattening:6.4.1 Well Casing Pipe—The well casing pipe shall have a pipe stiffness at 5 % deflection equal to that shown in Table 6 and Table 7 and shall deflect 60 % of the original diameter (flattening) without cracking, rupture, or other visible evidence of failure when tested in accordance with Test…
6 Apparatus6.1 Fig. 1 shows an example of the test apparatus that can be used in the performance of this test method. The apparatus requires a pressure vessel rated to a minimum of 690 kPa (100 psi). The vessel diameter should be 600 mm3. Other size vessels may be used but it is up to…
3 Apparatus3.1 Ambient temperaturesFor tests at ambient temperatures (see 5.2), a test room or water bath, capable of being maintained ata temperature to within ± 2°C.3.2 Elevated temperaturesFor tests at elevated temperatures, an air chamber or water bath, capable of being maintained at thespecified test temperature to within +3….-1C 3.3 Pressure control deviceA pressure control…
D.1 GeneralThermal analysis shall be used to characterize the uncured epoxy (powder, one-component liquid ortwo-component liquid) and the cured coating film.Differential scanning calorimetry (DSC) shall be used. Reference can be made to ISO 11357-2 for adescription of the general procedure and definitions. General handling and calibration shall be performed as inISO 11357-2 unless stated otherwise…